C55281 Copper vs. C92200 Bronze

Both C55281 copper and C92200 bronze are copper alloys. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 89% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is C55281 copper and the bottom bar is C92200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
110
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 40
41
Tensile Strength: Ultimate (UTS), MPa 190
280

Thermal Properties

Latent Heat of Fusion, J/g 190
190
Maximum Temperature: Mechanical, °C 200
170
Melting Completion (Liquidus), °C 810
990
Melting Onset (Solidus), °C 640
830
Specific Heat Capacity, J/kg-K 400
370
Thermal Expansion, µm/m-K 16
19

Otherwise Unclassified Properties

Density, g/cm3 8.7
8.7
Embodied Carbon, kg CO2/kg material 7.0
3.2
Embodied Energy, MJ/kg 110
52

Common Calculations

Stiffness to Weight: Axial, points 6.9
6.9
Stiffness to Weight: Bending, points 18
18
Strength to Weight: Axial, points 6.1
8.9
Strength to Weight: Bending, points 8.5
11
Thermal Shock Resistance, points 7.7
9.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Copper (Cu), % 88.5 to 89.4
86 to 90
Iron (Fe), % 0
0 to 0.25
Lead (Pb), % 0
1.0 to 2.0
Nickel (Ni), % 0
0 to 1.0
Phosphorus (P), % 5.8 to 6.2
0 to 1.5
Silicon (Si), % 0
0 to 0.0050
Silver (Ag), % 4.8 to 5.2
0
Sulfur (S), % 0
0 to 0.050
Tin (Sn), % 0
5.5 to 6.5
Zinc (Zn), % 0
3.0 to 5.0
Residuals, % 0
0 to 0.7