C55283 Copper vs. S44330 Stainless Steel
C55283 copper belongs to the copper alloys classification, while S44330 stainless steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is C55283 copper and the bottom bar is S44330 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Poisson's Ratio | 0.34 | |
| 0.27 |
| Shear Modulus, GPa | 39 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 440 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 990 |
| Melting Completion (Liquidus), °C | 720 | |
| 1440 |
| Melting Onset (Solidus), °C | 640 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 480 |
| Thermal Expansion, µm/m-K | 16 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 2.8 |
| Embodied Energy, MJ/kg | 120 | |
| 40 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 18 | |
| 25 |
| Strength to Weight: Axial, points | 6.1 | |
| 16 |
| Strength to Weight: Bending, points | 8.5 | |
| 17 |
| Thermal Shock Resistance, points | 8.0 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.025 |
| Chromium (Cr), % | 0 | |
| 20 to 23 |
| Copper (Cu), % | 86.2 to 87.2 | |
| 0.3 to 0.8 |
| Iron (Fe), % | 0 | |
| 72.5 to 79.7 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Niobium (Nb), % | 0 | |
| 0 to 0.8 |
| Nitrogen (N), % | 0 | |
| 0 to 0.025 |
| Phosphorus (P), % | 7.0 to 7.5 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 5.8 to 6.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0 to 0.8 |
| Residuals, % | 0 to 0.15 | |
| 0 |