C55283 Copper vs. Z41121 Zinc
C55283 copper belongs to the copper alloys classification, while Z41121 zinc belongs to the zinc alloys. There are 18 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is C55283 copper and the bottom bar is Z41121 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 87 |
| Poisson's Ratio | 0.34 | |
| 0.25 |
| Shear Modulus, GPa | 39 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 190 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 90 |
| Melting Completion (Liquidus), °C | 720 | |
| 410 |
| Melting Onset (Solidus), °C | 640 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Expansion, µm/m-K | 16 | |
| 26 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.6 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 2.8 |
| Embodied Energy, MJ/kg | 120 | |
| 54 |
Common Calculations
| Stiffness to Weight: Axial, points | 6.8 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 18 | |
| 23 |
| Strength to Weight: Axial, points | 6.1 | |
| 6.1 |
| Strength to Weight: Bending, points | 8.5 | |
| 9.3 |
| Thermal Shock Resistance, points | 8.0 | |
| 4.6 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.010 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 86.2 to 87.2 | |
| 0.080 to 0.49 |
| Iron (Fe), % | 0 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Phosphorus (P), % | 7.0 to 7.5 | |
| 0 |
| Silver (Ag), % | 5.8 to 6.2 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 | |
| 0.050 to 0.18 |
| Zinc (Zn), % | 0 | |
| 99.292 to 99.87 |
| Residuals, % | 0 to 0.15 | |
| 0 |