C61000 Bronze vs. 7003 Aluminum
C61000 bronze belongs to the copper alloys classification, while 7003 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is C61000 bronze and the bottom bar is 7003 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 70 |
| Elongation at Break, % | 29 to 50 | |
| 11 |
| Poisson's Ratio | 0.34 | |
| 0.32 |
| Shear Modulus, GPa | 42 | |
| 26 |
| Shear Strength, MPa | 280 to 300 | |
| 210 to 230 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 460 | |
| 350 to 390 |
| Tensile Strength: Yield (Proof), MPa | 150 to 190 | |
| 300 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 380 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 200 |
| Melting Completion (Liquidus), °C | 1040 | |
| 630 |
| Melting Onset (Solidus), °C | 990 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 870 |
| Thermal Conductivity, W/m-K | 69 | |
| 150 |
| Thermal Expansion, µm/m-K | 18 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 36 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 16 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 9.5 |
| Density, g/cm3 | 8.5 | |
| 2.9 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 8.1 |
| Embodied Energy, MJ/kg | 49 | |
| 150 |
| Embodied Water, L/kg | 370 | |
| 1140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 160 | |
| 37 to 41 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 160 | |
| 630 to 710 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 47 |
| Strength to Weight: Axial, points | 13 to 15 | |
| 33 to 37 |
| Strength to Weight: Bending, points | 14 to 16 | |
| 37 to 40 |
| Thermal Diffusivity, mm2/s | 19 | |
| 59 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 15 to 17 |
Alloy Composition
| Aluminum (Al), % | 6.0 to 8.5 | |
| 90.6 to 94.5 |
| Chromium (Cr), % | 0 | |
| 0 to 0.2 |
| Copper (Cu), % | 90.2 to 94 | |
| 0 to 0.2 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.35 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0.5 to 1.0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.3 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.3 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 to 0.2 | |
| 5.0 to 6.5 |
| Zirconium (Zr), % | 0 | |
| 0.050 to 0.25 |
| Residuals, % | 0 | |
| 0 to 0.15 |