C61000 Bronze vs. C32000 Brass
Both C61000 bronze and C32000 brass are copper alloys. They have 85% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is C61000 bronze and the bottom bar is C32000 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 29 to 50 | |
| 6.8 to 29 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 42 | |
| 41 |
| Shear Strength, MPa | 280 to 300 | |
| 180 to 280 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 460 | |
| 270 to 470 |
| Tensile Strength: Yield (Proof), MPa | 150 to 190 | |
| 78 to 390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 170 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1020 |
| Melting Onset (Solidus), °C | 990 | |
| 990 |
| Specific Heat Capacity, J/kg-K | 420 | |
| 380 |
| Thermal Conductivity, W/m-K | 69 | |
| 160 |
| Thermal Expansion, µm/m-K | 18 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 36 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 16 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 28 |
| Density, g/cm3 | 8.5 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 2.6 |
| Embodied Energy, MJ/kg | 49 | |
| 42 |
| Embodied Water, L/kg | 370 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 160 | |
| 30 to 59 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 160 | |
| 28 to 680 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 13 to 15 | |
| 8.8 to 15 |
| Strength to Weight: Bending, points | 14 to 16 | |
| 11 to 16 |
| Thermal Diffusivity, mm2/s | 19 | |
| 47 |
| Thermal Shock Resistance, points | 14 to 16 | |
| 9.5 to 16 |
Alloy Composition
| Aluminum (Al), % | 6.0 to 8.5 | |
| 0 |
| Copper (Cu), % | 90.2 to 94 | |
| 83.5 to 86.5 |
| Iron (Fe), % | 0 to 0.5 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.020 | |
| 1.5 to 2.2 |
| Nickel (Ni), % | 0 | |
| 0 to 0.25 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Zinc (Zn), % | 0 to 0.2 | |
| 10.6 to 15 |
| Residuals, % | 0 | |
| 0 to 0.4 |