C61500 Bronze vs. EN 1.0597 Cast Steel
C61500 bronze belongs to the copper alloys classification, while EN 1.0597 cast steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C61500 bronze and the bottom bar is EN 1.0597 cast steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 3.0 to 55 | |
| 18 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 970 | |
| 670 |
| Tensile Strength: Yield (Proof), MPa | 150 to 720 | |
| 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 400 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1470 |
| Melting Onset (Solidus), °C | 1030 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 470 |
| Thermal Conductivity, W/m-K | 58 | |
| 53 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 7.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 13 | |
| 8.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 1.7 |
| Density, g/cm3 | 8.4 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 1.4 |
| Embodied Energy, MJ/kg | 52 | |
| 18 |
| Embodied Water, L/kg | 380 | |
| 45 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 to 200 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 2310 | |
| 430 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 32 | |
| 24 |
| Strength to Weight: Bending, points | 16 to 26 | |
| 22 |
| Thermal Diffusivity, mm2/s | 16 | |
| 14 |
| Thermal Shock Resistance, points | 17 to 34 | |
| 21 |
Alloy Composition
| Aluminum (Al), % | 7.7 to 8.3 | |
| 0 |
| Copper (Cu), % | 89 to 90.5 | |
| 0 |
| Iron (Fe), % | 0 | |
| 99.935 to 100 |
| Lead (Pb), % | 0 to 0.015 | |
| 0 |
| Nickel (Ni), % | 1.8 to 2.2 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.5 | |
| 0 |