C61500 Bronze vs. N08221 Nickel
C61500 bronze belongs to the copper alloys classification, while N08221 nickel belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C61500 bronze and the bottom bar is N08221 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 3.0 to 55 | |
| 34 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 79 |
| Shear Strength, MPa | 350 to 550 | |
| 410 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 970 | |
| 610 |
| Tensile Strength: Yield (Proof), MPa | 150 to 720 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 980 |
| Melting Completion (Liquidus), °C | 1040 | |
| 1440 |
| Melting Onset (Solidus), °C | 1030 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 460 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 44 |
| Density, g/cm3 | 8.4 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 7.9 |
| Embodied Energy, MJ/kg | 52 | |
| 110 |
| Embodied Water, L/kg | 380 | |
| 240 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 27 to 200 | |
| 170 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 2310 | |
| 170 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 32 | |
| 21 |
| Strength to Weight: Bending, points | 16 to 26 | |
| 19 |
| Thermal Shock Resistance, points | 17 to 34 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 7.7 to 8.3 | |
| 0 to 0.2 |
| Carbon (C), % | 0 | |
| 0 to 0.025 |
| Chromium (Cr), % | 0 | |
| 20 to 22 |
| Copper (Cu), % | 89 to 90.5 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 0 | |
| 22 to 33.9 |
| Lead (Pb), % | 0 to 0.015 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 5.0 to 6.5 |
| Nickel (Ni), % | 1.8 to 2.2 | |
| 39 to 46 |
| Silicon (Si), % | 0 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 | |
| 0.6 to 1.0 |
| Residuals, % | 0 to 0.5 | |
| 0 |