C61800 Bronze vs. AWS E80C-B6

C61800 bronze belongs to the copper alloys classification, while AWS E80C-B6 belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is C61800 bronze and the bottom bar is AWS E80C-B6.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Elongation at Break, % 26
19
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 44
74
Tensile Strength: Ultimate (UTS), MPa 740
630
Tensile Strength: Yield (Proof), MPa 310
530

Thermal Properties

Latent Heat of Fusion, J/g 230
260
Melting Completion (Liquidus), °C 1050
1450
Melting Onset (Solidus), °C 1040
1410
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 64
39
Thermal Expansion, µm/m-K 18
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
8.2
Electrical Conductivity: Equal Weight (Specific), % IACS 14
9.5

Otherwise Unclassified Properties

Base Metal Price, % relative 28
4.7
Density, g/cm3 8.3
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.8
Embodied Energy, MJ/kg 52
25
Embodied Water, L/kg 390
71

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
120
Resilience: Unit (Modulus of Resilience), kJ/m3 420
730
Stiffness to Weight: Axial, points 7.5
14
Stiffness to Weight: Bending, points 19
25
Strength to Weight: Axial, points 25
22
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 18
11
Thermal Shock Resistance, points 26
18

Alloy Composition

Aluminum (Al), % 8.5 to 11
0
Carbon (C), % 0
0 to 0.1
Chromium (Cr), % 0
4.5 to 6.0
Copper (Cu), % 86.9 to 91
0 to 0.35
Iron (Fe), % 0.5 to 1.5
90.1 to 94.4
Lead (Pb), % 0 to 0.020
0
Manganese (Mn), % 0
0.4 to 1.0
Molybdenum (Mo), % 0
0.45 to 0.65
Nickel (Ni), % 0
0 to 0.6
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.1
0.25 to 0.6
Sulfur (S), % 0
0 to 0.025
Vanadium (V), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.020
0
Residuals, % 0
0 to 0.5