C62300 Bronze vs. C96700 Copper
Both C62300 bronze and C96700 copper are copper alloys. They have 67% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C62300 bronze and the bottom bar is C96700 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 140 |
| Elongation at Break, % | 18 to 32 | |
| 10 |
| Poisson's Ratio | 0.34 | |
| 0.33 |
| Shear Modulus, GPa | 43 | |
| 53 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 630 | |
| 1210 |
| Tensile Strength: Yield (Proof), MPa | 230 to 310 | |
| 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 220 | |
| 310 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1170 |
| Melting Onset (Solidus), °C | 1040 | |
| 1110 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 400 |
| Thermal Conductivity, W/m-K | 54 | |
| 30 |
| Thermal Expansion, µm/m-K | 18 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 28 | |
| 90 |
| Density, g/cm3 | 8.3 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 9.5 |
| Embodied Energy, MJ/kg | 52 | |
| 140 |
| Embodied Water, L/kg | 390 | |
| 280 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 95 to 150 | |
| 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 430 | |
| 1080 |
| Stiffness to Weight: Axial, points | 7.6 | |
| 8.9 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 19 to 21 | |
| 38 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 29 |
| Thermal Diffusivity, mm2/s | 15 | |
| 8.5 |
| Thermal Shock Resistance, points | 20 to 22 | |
| 40 |
Alloy Composition
| Aluminum (Al), % | 8.5 to 10 | |
| 0 |
| Beryllium (Be), % | 0 | |
| 1.1 to 1.2 |
| Copper (Cu), % | 83.2 to 89.5 | |
| 62.4 to 68.8 |
| Iron (Fe), % | 2.0 to 4.0 | |
| 0.4 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 0.5 | |
| 0.4 to 1.0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 29 to 33 |
| Silicon (Si), % | 0 to 0.25 | |
| 0 to 0.15 |
| Tin (Sn), % | 0 to 0.6 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.35 |
| Zirconium (Zr), % | 0 | |
| 0.15 to 0.35 |
| Residuals, % | 0 | |
| 0 to 0.5 |