C63200 Bronze vs. Nickel 689
C63200 bronze belongs to the copper alloys classification, while nickel 689 belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C63200 bronze and the bottom bar is nickel 689.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 210 |
| Elongation at Break, % | 17 to 18 | |
| 23 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 44 | |
| 80 |
| Shear Strength, MPa | 390 to 440 | |
| 790 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 710 | |
| 1250 |
| Tensile Strength: Yield (Proof), MPa | 310 to 350 | |
| 690 |
Thermal Properties
| Latent Heat of Fusion, J/g | 230 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 230 | |
| 990 |
| Melting Completion (Liquidus), °C | 1060 | |
| 1440 |
| Melting Onset (Solidus), °C | 1040 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 450 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 70 |
| Density, g/cm3 | 8.3 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 11 |
| Embodied Energy, MJ/kg | 55 | |
| 150 |
| Embodied Water, L/kg | 380 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 95 to 99 | |
| 240 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 400 to 510 | |
| 1170 |
| Stiffness to Weight: Axial, points | 7.9 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 23 |
| Strength to Weight: Axial, points | 21 to 24 | |
| 41 |
| Strength to Weight: Bending, points | 20 to 21 | |
| 30 |
| Thermal Shock Resistance, points | 22 to 24 | |
| 35 |
Alloy Composition
| Aluminum (Al), % | 8.7 to 9.5 | |
| 0.75 to 1.3 |
| Boron (B), % | 0 | |
| 0.0030 to 0.010 |
| Carbon (C), % | 0 | |
| 0.1 to 0.2 |
| Chromium (Cr), % | 0 | |
| 18 to 20 |
| Cobalt (Co), % | 0 | |
| 9.0 to 11 |
| Copper (Cu), % | 78.8 to 82.6 | |
| 0 |
| Iron (Fe), % | 3.5 to 4.3 | |
| 0 to 5.0 |
| Lead (Pb), % | 0 to 0.020 | |
| 0 |
| Manganese (Mn), % | 1.2 to 2.0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 9.0 to 10.5 |
| Nickel (Ni), % | 4.0 to 4.8 | |
| 48.3 to 60.9 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 2.3 to 2.8 |
| Residuals, % | 0 to 0.5 | |
| 0 |