C63200 Bronze vs. R60704 Alloy

C63200 bronze belongs to the copper alloys classification, while R60704 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is C63200 bronze and the bottom bar is R60704 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
97
Elongation at Break, % 17 to 18
16
Poisson's Ratio 0.34
0.34
Shear Modulus, GPa 44
36
Tensile Strength: Ultimate (UTS), MPa 640 to 710
470
Tensile Strength: Yield (Proof), MPa 310 to 350
270

Thermal Properties

Latent Heat of Fusion, J/g 230
240
Specific Heat Capacity, J/kg-K 440
270
Thermal Conductivity, W/m-K 35
22
Thermal Expansion, µm/m-K 18
6.0

Otherwise Unclassified Properties

Density, g/cm3 8.3
6.7
Embodied Water, L/kg 380
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95 to 99
64
Resilience: Unit (Modulus of Resilience), kJ/m3 400 to 510
370
Stiffness to Weight: Axial, points 7.9
8.1
Stiffness to Weight: Bending, points 20
23
Strength to Weight: Axial, points 21 to 24
20
Strength to Weight: Bending, points 20 to 21
20
Thermal Diffusivity, mm2/s 9.6
12
Thermal Shock Resistance, points 22 to 24
58

Alloy Composition

Aluminum (Al), % 8.7 to 9.5
0
Carbon (C), % 0
0 to 0.050
Chromium (Cr), % 0
0.2 to 0.4
Copper (Cu), % 78.8 to 82.6
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 3.5 to 4.3
0.2 to 0.4
Lead (Pb), % 0 to 0.020
0
Manganese (Mn), % 1.2 to 2.0
0
Nickel (Ni), % 4.0 to 4.8
0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.18
Silicon (Si), % 0 to 0.1
0
Tin (Sn), % 0
1.0 to 2.0
Zirconium (Zr), % 0
93 to 98.8
Residuals, % 0 to 0.5
0