C63800 Bronze vs. C54400 Bronze
Both C63800 bronze and C54400 bronze are copper alloys. They have 89% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C63800 bronze and the bottom bar is C54400 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Rockwell B Hardness | 94 to 110 | |
| 67 to 93 |
| Rockwell Superficial 30T Hardness | 74 to 93 | |
| 33 to 79 |
| Shear Modulus, GPa | 43 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 1010 | |
| 330 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 170 |
| Melting Completion (Liquidus), °C | 1030 | |
| 1000 |
| Melting Onset (Solidus), °C | 1000 | |
| 930 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 370 |
| Thermal Conductivity, W/m-K | 40 | |
| 86 |
| Thermal Expansion, µm/m-K | 17 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 19 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 30 | |
| 31 |
| Density, g/cm3 | 8.6 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.9 |
| Embodied Energy, MJ/kg | 45 | |
| 48 |
| Embodied Water, L/kg | 330 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 15 to 33 | |
| 10 to 22 |
| Strength to Weight: Bending, points | 15 to 26 | |
| 12 to 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 26 |
| Thermal Shock Resistance, points | 17 to 36 | |
| 12 to 26 |
Alloy Composition
| Aluminum (Al), % | 2.5 to 3.1 | |
| 0 |
| Cobalt (Co), % | 0.25 to 0.55 | |
| 0 |
| Copper (Cu), % | 92.4 to 95.8 | |
| 85.4 to 91.5 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 to 0.050 | |
| 3.5 to 4.5 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.010 to 0.5 |
| Silicon (Si), % | 1.5 to 2.1 | |
| 0 |
| Tin (Sn), % | 0 | |
| 3.5 to 4.5 |
| Zinc (Zn), % | 0 to 0.8 | |
| 1.5 to 4.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |