C64200 Bronze vs. EN 2.4815 Cast Nickel
C64200 bronze belongs to the copper alloys classification, while EN 2.4815 cast nickel belongs to the nickel alloys. There are 28 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C64200 bronze and the bottom bar is EN 2.4815 cast nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 14 to 35 | |
| 3.4 |
| Poisson's Ratio | 0.34 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 540 to 640 | |
| 460 |
| Tensile Strength: Yield (Proof), MPa | 230 to 320 | |
| 220 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1000 | |
| 1510 |
| Melting Onset (Solidus), °C | 980 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 470 |
| Thermal Conductivity, W/m-K | 45 | |
| 25 |
| Thermal Expansion, µm/m-K | 18 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 3.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 47 |
| Density, g/cm3 | 8.3 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 7.9 |
| Embodied Energy, MJ/kg | 50 | |
| 110 |
| Embodied Water, L/kg | 370 | |
| 230 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 73 to 170 | |
| 13 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 240 to 470 | |
| 130 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 18 to 21 | |
| 15 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 16 |
| Thermal Diffusivity, mm2/s | 13 | |
| 6.4 |
| Thermal Shock Resistance, points | 20 to 23 | |
| 17 |
Alloy Composition
| Aluminum (Al), % | 6.3 to 7.6 | |
| 0 |
| Arsenic (As), % | 0 to 0.15 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.35 to 0.65 |
| Chromium (Cr), % | 0 | |
| 12 to 18 |
| Copper (Cu), % | 88.2 to 92.2 | |
| 0 |
| Iron (Fe), % | 0 to 0.3 | |
| 9.8 to 28.7 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.25 | |
| 58 to 66 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 1.5 to 2.2 | |
| 1.0 to 2.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |