C64200 Bronze vs. SAE-AISI H19 Steel

C64200 bronze belongs to the copper alloys classification, while SAE-AISI H19 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is C64200 bronze and the bottom bar is SAE-AISI H19 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
190
Poisson's Ratio 0.34
0.29
Shear Modulus, GPa 42
75
Tensile Strength: Ultimate (UTS), MPa 540 to 640
720 to 1990

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Melting Completion (Liquidus), °C 1000
1540
Melting Onset (Solidus), °C 980
1490
Specific Heat Capacity, J/kg-K 430
460
Thermal Conductivity, W/m-K 45
29
Thermal Expansion, µm/m-K 18
12

Otherwise Unclassified Properties

Base Metal Price, % relative 29
22
Density, g/cm3 8.3
8.2
Embodied Carbon, kg CO2/kg material 3.0
7.5
Embodied Energy, MJ/kg 50
110
Embodied Water, L/kg 370
110

Common Calculations

Stiffness to Weight: Axial, points 7.5
13
Stiffness to Weight: Bending, points 19
24
Strength to Weight: Axial, points 18 to 21
24 to 68
Strength to Weight: Bending, points 18 to 20
22 to 43
Thermal Diffusivity, mm2/s 13
7.9
Thermal Shock Resistance, points 20 to 23
21 to 59

Alloy Composition

Aluminum (Al), % 6.3 to 7.6
0
Arsenic (As), % 0 to 0.15
0
Carbon (C), % 0
0.32 to 0.45
Chromium (Cr), % 0
4.0 to 4.8
Cobalt (Co), % 0
4.0 to 4.5
Copper (Cu), % 88.2 to 92.2
0 to 0.25
Iron (Fe), % 0 to 0.3
81.4 to 85.5
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 0 to 0.1
0.2 to 0.5
Molybdenum (Mo), % 0
0.3 to 0.55
Nickel (Ni), % 0 to 0.25
0 to 0.3
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 1.5 to 2.2
0.2 to 0.5
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 0 to 0.2
0
Tungsten (W), % 0
3.8 to 4.5
Vanadium (V), % 0
1.8 to 2.2
Zinc (Zn), % 0 to 0.5
0
Residuals, % 0 to 0.5
0