C64700 Bronze vs. C34500 Brass
Both C64700 bronze and C34500 brass are copper alloys. They have 64% of their average alloy composition in common.
For each property being compared, the top bar is C64700 bronze and the bottom bar is C34500 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 100 |
| Elongation at Break, % | 9.0 | |
| 12 to 28 |
| Poisson's Ratio | 0.34 | |
| 0.31 |
| Shear Modulus, GPa | 44 | |
| 40 |
| Shear Strength, MPa | 390 | |
| 220 to 260 |
| Tensile Strength: Ultimate (UTS), MPa | 660 | |
| 340 to 430 |
| Tensile Strength: Yield (Proof), MPa | 560 | |
| 120 to 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 120 |
| Melting Completion (Liquidus), °C | 1090 | |
| 910 |
| Melting Onset (Solidus), °C | 1030 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 380 |
| Thermal Conductivity, W/m-K | 210 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 38 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 38 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 24 |
| Density, g/cm3 | 8.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 43 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 57 | |
| 42 to 75 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1370 | |
| 69 to 160 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 21 | |
| 12 to 15 |
| Strength to Weight: Bending, points | 19 | |
| 13 to 16 |
| Thermal Diffusivity, mm2/s | 59 | |
| 37 |
| Thermal Shock Resistance, points | 24 | |
| 11 to 14 |
Alloy Composition
| Copper (Cu), % | 95.8 to 98 | |
| 62 to 65 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.15 |
| Lead (Pb), % | 0 to 0.1 | |
| 1.5 to 2.5 |
| Nickel (Ni), % | 1.6 to 2.2 | |
| 0 |
| Silicon (Si), % | 0.4 to 0.8 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 32 to 36.5 |
| Residuals, % | 0 | |
| 0 to 0.4 |