C65400 Bronze vs. C19025 Copper
Both C65400 bronze and C19025 copper are copper alloys. They have a very high 96% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C65400 bronze and the bottom bar is C19025 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 2.6 to 47 | |
| 8.0 to 17 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 43 |
| Shear Strength, MPa | 350 to 530 | |
| 300 to 360 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1060 | |
| 480 to 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1020 | |
| 1080 |
| Melting Onset (Solidus), °C | 960 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 380 |
| Thermal Conductivity, W/m-K | 36 | |
| 160 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 40 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.3 | |
| 40 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 31 |
| Density, g/cm3 | 8.7 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 45 | |
| 44 |
| Embodied Water, L/kg | 310 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 16 to 34 | |
| 15 to 19 |
| Strength to Weight: Bending, points | 16 to 27 | |
| 15 to 18 |
| Thermal Diffusivity, mm2/s | 10 | |
| 47 |
| Thermal Shock Resistance, points | 18 to 39 | |
| 17 to 22 |
Alloy Composition
| Chromium (Cr), % | 0.010 to 0.12 | |
| 0 |
| Copper (Cu), % | 93.8 to 96.1 | |
| 97.1 to 98.5 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0.8 to 1.2 |
| Phosphorus (P), % | 0 | |
| 0.030 to 0.070 |
| Silicon (Si), % | 2.7 to 3.4 | |
| 0 |
| Tin (Sn), % | 1.2 to 1.9 | |
| 0.7 to 1.1 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.3 |