C65400 Bronze vs. C55282 Copper
Both C65400 bronze and C55282 copper are copper alloys. They have 88% of their average alloy composition in common. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is C65400 bronze and the bottom bar is C55282 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 43 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 1060 | |
| 180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 190 |
| Maximum Temperature: Mechanical, °C | 200 | |
| 200 |
| Melting Completion (Liquidus), °C | 1020 | |
| 770 |
| Melting Onset (Solidus), °C | 960 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 400 |
| Thermal Expansion, µm/m-K | 17 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 7.0 |
| Embodied Energy, MJ/kg | 45 | |
| 110 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.3 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 16 to 34 | |
| 5.8 |
| Strength to Weight: Bending, points | 16 to 27 | |
| 8.2 |
| Thermal Shock Resistance, points | 18 to 39 | |
| 7.4 |
Alloy Composition
| Chromium (Cr), % | 0.010 to 0.12 | |
| 0 |
| Copper (Cu), % | 93.8 to 96.1 | |
| 87.7 to 88.7 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 6.5 to 7.0 |
| Silicon (Si), % | 2.7 to 3.4 | |
| 0 |
| Silver (Ag), % | 0 | |
| 4.8 to 5.2 |
| Tin (Sn), % | 1.2 to 1.9 | |
| 0 |
| Zinc (Zn), % | 0 to 0.5 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |