C66200 Brass vs. Class 2 Tungsten
C66200 brass belongs to the copper alloys classification, while class 2 tungsten belongs to the otherwise unclassified metals. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C66200 brass and the bottom bar is class 2 tungsten.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 260 |
| Elongation at Break, % | 8.0 to 15 | |
| 5.7 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 100 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 520 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 410 to 480 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 160 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 120 |
| Thermal Conductivity, W/m-K | 150 | |
| 20 |
| Thermal Expansion, µm/m-K | 18 | |
| 4.6 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 36 | |
| 7.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 15 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 23 |
| Embodied Energy, MJ/kg | 43 | |
| 350 |
| Embodied Water, L/kg | 320 | |
| 140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 to 66 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 760 to 1030 | |
| 640 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 9.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 14 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 16 |
| Strength to Weight: Bending, points | 15 to 16 | |
| 13 |
| Thermal Diffusivity, mm2/s | 45 | |
| 11 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 52 |
Alloy Composition
| Copper (Cu), % | 86.6 to 91 | |
| 0 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Nickel (Ni), % | 0.3 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0.050 to 0.2 | |
| 0 |
| Tin (Sn), % | 0.2 to 0.7 | |
| 0 |
| Tungsten (W), % | 0 | |
| 92.5 |
| Zinc (Zn), % | 6.5 to 12.9 | |
| 0 |
| Residuals, % | 0 | |
| 7.5 |