C66200 Brass vs. C11300 Copper
Both C66200 brass and C11300 copper are copper alloys. They have 89% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C66200 brass and the bottom bar is C11300 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 8.0 to 15 | |
| 2.3 to 50 |
| Poisson's Ratio | 0.33 | |
| 0.34 |
| Shear Modulus, GPa | 42 | |
| 43 |
| Shear Strength, MPa | 270 to 300 | |
| 160 to 240 |
| Tensile Strength: Ultimate (UTS), MPa | 450 to 520 | |
| 230 to 410 |
| Tensile Strength: Yield (Proof), MPa | 410 to 480 | |
| 77 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 200 |
| Melting Completion (Liquidus), °C | 1070 | |
| 1080 |
| Melting Onset (Solidus), °C | 1030 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 150 | |
| 390 |
| Thermal Expansion, µm/m-K | 18 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 36 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 32 |
| Density, g/cm3 | 8.7 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 43 | |
| 42 |
| Embodied Water, L/kg | 320 | |
| 340 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 to 66 | |
| 8.5 to 91 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 760 to 1030 | |
| 25 to 690 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 7.2 to 13 |
| Strength to Weight: Bending, points | 15 to 16 | |
| 9.4 to 14 |
| Thermal Diffusivity, mm2/s | 45 | |
| 110 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 8.2 to 15 |
Alloy Composition
| Copper (Cu), % | 86.6 to 91 | |
| 99.85 to 99.973 |
| Iron (Fe), % | 0 to 0.050 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Nickel (Ni), % | 0.3 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0.050 to 0.2 | |
| 0 |
| Silver (Ag), % | 0 | |
| 0.027 to 0.050 |
| Tin (Sn), % | 0.2 to 0.7 | |
| 0 |
| Zinc (Zn), % | 6.5 to 12.9 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.1 |