C66300 Brass vs. EN 1.7725 Steel
C66300 brass belongs to the copper alloys classification, while EN 1.7725 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is C66300 brass and the bottom bar is EN 1.7725 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 2.3 to 22 | |
| 14 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 810 | |
| 830 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 400 to 800 | |
| 610 to 860 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 440 |
| Melting Completion (Liquidus), °C | 1050 | |
| 1460 |
| Melting Onset (Solidus), °C | 1000 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 470 |
| Thermal Conductivity, W/m-K | 110 | |
| 39 |
| Thermal Expansion, µm/m-K | 18 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 26 | |
| 8.6 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 2.9 |
| Density, g/cm3 | 8.6 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.8 |
| Embodied Energy, MJ/kg | 46 | |
| 24 |
| Embodied Water, L/kg | 320 | |
| 54 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 17 to 98 | |
| 110 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 710 to 2850 | |
| 980 to 1940 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 26 | |
| 29 to 35 |
| Strength to Weight: Bending, points | 15 to 22 | |
| 25 to 28 |
| Thermal Diffusivity, mm2/s | 32 | |
| 11 |
| Thermal Shock Resistance, points | 16 to 28 | |
| 24 to 29 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.27 to 0.34 |
| Chromium (Cr), % | 0 | |
| 1.3 to 1.7 |
| Cobalt (Co), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 84.5 to 87.5 | |
| 0 |
| Iron (Fe), % | 1.4 to 2.4 | |
| 95.7 to 97.5 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.6 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.3 to 0.5 |
| Phosphorus (P), % | 0 to 0.35 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 1.5 to 3.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.050 to 0.15 |
| Zinc (Zn), % | 6.0 to 12.8 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |