C66300 Brass vs. ZA-12
C66300 brass belongs to the copper alloys classification, while ZA-12 belongs to the zinc alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C66300 brass and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 83 |
| Elongation at Break, % | 2.3 to 22 | |
| 1.6 to 5.3 |
| Poisson's Ratio | 0.33 | |
| 0.26 |
| Shear Modulus, GPa | 42 | |
| 33 |
| Shear Strength, MPa | 290 to 470 | |
| 240 to 300 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 810 | |
| 260 to 400 |
| Tensile Strength: Yield (Proof), MPa | 400 to 800 | |
| 210 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 200 | |
| 120 |
| Maximum Temperature: Mechanical, °C | 180 | |
| 100 |
| Melting Completion (Liquidus), °C | 1050 | |
| 430 |
| Melting Onset (Solidus), °C | 1000 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 450 |
| Thermal Conductivity, W/m-K | 110 | |
| 120 |
| Thermal Expansion, µm/m-K | 18 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 26 | |
| 42 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 29 | |
| 11 |
| Density, g/cm3 | 8.6 | |
| 6.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.4 |
| Embodied Energy, MJ/kg | 46 | |
| 64 |
| Embodied Water, L/kg | 320 | |
| 440 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 17 to 98 | |
| 4.0 to 20 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 710 to 2850 | |
| 260 to 620 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 26 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 15 to 22 | |
| 15 to 20 |
| Thermal Diffusivity, mm2/s | 32 | |
| 43 |
| Thermal Shock Resistance, points | 16 to 28 | |
| 9.4 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10.5 to 11.5 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Cobalt (Co), % | 0 to 0.2 | |
| 0 |
| Copper (Cu), % | 84.5 to 87.5 | |
| 0.5 to 1.2 |
| Iron (Fe), % | 1.4 to 2.4 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.015 to 0.030 |
| Nickel (Ni), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.35 | |
| 0 |
| Silicon (Si), % | 0 | |
| 0 to 0.060 |
| Tin (Sn), % | 1.5 to 3.0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 6.0 to 12.8 | |
| 87.1 to 89 |
| Residuals, % | 0 to 0.5 | |
| 0 |