C66700 Brass vs. 92-silver 8-tin-oxide
C66700 brass belongs to the copper alloys classification, while 92-silver 8-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (25, in this case) are not shown.
For each property being compared, the top bar is C66700 brass and the bottom bar is 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 17 | |
| 76 to 80 |
| Elongation at Break, % | 2.0 to 58 | |
| 32 to 34 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 150 | |
| 62 to 110 |
| Shear Strength, MPa | 250 to 530 | |
| 150 to 210 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 690 | |
| 230 to 320 |
| Tensile Strength: Yield (Proof), MPa | 100 to 640 | |
| 120 to 300 |