C66700 Brass vs. AISI 205 Stainless Steel
C66700 brass belongs to the copper alloys classification, while AISI 205 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C66700 brass and the bottom bar is AISI 205 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 110 | |
200 |
Elongation at Break, % | 2.0 to 58 | |
11 to 51 |
Poisson's Ratio | 0.31 | |
0.28 |
Shear Modulus, GPa | 41 | |
77 |
Shear Strength, MPa | 250 to 530 | |
560 to 850 |
Tensile Strength: Ultimate (UTS), MPa | 340 to 690 | |
800 to 1430 |
Tensile Strength: Yield (Proof), MPa | 100 to 640 | |
450 to 1100 |
Thermal Properties
Latent Heat of Fusion, J/g | 180 | |
280 |
Maximum Temperature: Mechanical, °C | 140 | |
880 |
Melting Completion (Liquidus), °C | 1090 | |
1380 |
Melting Onset (Solidus), °C | 1050 | |
1340 |
Specific Heat Capacity, J/kg-K | 390 | |
480 |
Thermal Expansion, µm/m-K | 20 | |
18 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 25 | |
11 |
Density, g/cm3 | 8.2 | |
7.6 |
Embodied Carbon, kg CO2/kg material | 2.7 | |
2.6 |
Embodied Energy, MJ/kg | 45 | |
37 |
Embodied Water, L/kg | 320 | |
150 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 150 | |
150 to 430 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 49 to 1900 | |
510 to 3060 |
Stiffness to Weight: Axial, points | 7.3 | |
14 |
Stiffness to Weight: Bending, points | 19 | |
26 |
Strength to Weight: Axial, points | 11 to 23 | |
29 to 52 |
Strength to Weight: Bending, points | 13 to 21 | |
25 to 37 |
Thermal Shock Resistance, points | 11 to 23 | |
16 to 29 |
Alloy Composition
Carbon (C), % | 0 | |
0.12 to 0.25 |
Chromium (Cr), % | 0 | |
16.5 to 18.5 |
Copper (Cu), % | 68.5 to 71.5 | |
0 |
Iron (Fe), % | 0 to 0.1 | |
62.6 to 68.1 |
Lead (Pb), % | 0 to 0.070 | |
0 |
Manganese (Mn), % | 0.8 to 1.5 | |
14 to 15.5 |
Nickel (Ni), % | 0 | |
1.0 to 1.7 |
Nitrogen (N), % | 0 | |
0.32 to 0.4 |
Phosphorus (P), % | 0 | |
0 to 0.060 |
Silicon (Si), % | 0 | |
0 to 1.0 |
Sulfur (S), % | 0 | |
0 to 0.030 |
Zinc (Zn), % | 26.3 to 30.7 | |
0 |
Residuals, % | 0 to 0.5 | |
0 |