C66700 Brass vs. C14200 Copper
Both C66700 brass and C14200 copper are copper alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C66700 brass and the bottom bar is C14200 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 2.0 to 58 | |
| 8.0 to 45 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Rockwell B Hardness | 57 to 93 | |
| 35 to 60 |
| Rockwell Superficial 30T Hardness | 30 to 90 | |
| 45 to 63 |
| Shear Modulus, GPa | 41 | |
| 43 |
| Shear Strength, MPa | 250 to 530 | |
| 150 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 690 | |
| 220 to 370 |
| Tensile Strength: Yield (Proof), MPa | 100 to 640 | |
| 75 to 340 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 200 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1080 |
| Melting Onset (Solidus), °C | 1050 | |
| 1030 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 97 | |
| 190 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 17 | |
| 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 45 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 31 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 45 | |
| 41 |
| Embodied Water, L/kg | 320 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 150 | |
| 29 to 83 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 49 to 1900 | |
| 24 to 500 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 19 | |
| 18 |
| Strength to Weight: Axial, points | 11 to 23 | |
| 6.8 to 11 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 9.1 to 13 |
| Thermal Diffusivity, mm2/s | 30 | |
| 56 |
| Thermal Shock Resistance, points | 11 to 23 | |
| 7.9 to 13 |
Alloy Composition
| Arsenic (As), % | 0 | |
| 0.15 to 0.5 |
| Copper (Cu), % | 68.5 to 71.5 | |
| 99.4 to 99.835 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Manganese (Mn), % | 0.8 to 1.5 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.015 to 0.040 |
| Zinc (Zn), % | 26.3 to 30.7 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |