C66700 Brass vs. C66100 Bronze
Both C66700 brass and C66100 bronze are copper alloys. They have 72% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C66700 brass and the bottom bar is C66100 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 2.0 to 58 | |
| 8.0 to 40 |
| Poisson's Ratio | 0.31 | |
| 0.34 |
| Shear Modulus, GPa | 41 | |
| 43 |
| Shear Strength, MPa | 250 to 530 | |
| 280 to 460 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 690 | |
| 410 to 790 |
| Tensile Strength: Yield (Proof), MPa | 100 to 640 | |
| 120 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 140 | |
| 200 |
| Melting Completion (Liquidus), °C | 1090 | |
| 1050 |
| Melting Onset (Solidus), °C | 1050 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 400 |
| Thermal Conductivity, W/m-K | 97 | |
| 34 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 25 | |
| 29 |
| Density, g/cm3 | 8.2 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.6 |
| Embodied Energy, MJ/kg | 45 | |
| 42 |
| Embodied Water, L/kg | 320 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 13 to 150 | |
| 53 to 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 49 to 1900 | |
| 60 to 790 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 19 | |
| 19 |
| Strength to Weight: Axial, points | 11 to 23 | |
| 13 to 25 |
| Strength to Weight: Bending, points | 13 to 21 | |
| 14 to 22 |
| Thermal Diffusivity, mm2/s | 30 | |
| 9.7 |
| Thermal Shock Resistance, points | 11 to 23 | |
| 15 to 29 |
Alloy Composition
| Copper (Cu), % | 68.5 to 71.5 | |
| 92 to 97 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 to 0.25 |
| Lead (Pb), % | 0 to 0.070 | |
| 0.2 to 0.8 |
| Manganese (Mn), % | 0.8 to 1.5 | |
| 0 to 1.5 |
| Silicon (Si), % | 0 | |
| 2.8 to 3.5 |
| Zinc (Zn), % | 26.3 to 30.7 | |
| 0 to 1.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |