C66900 Brass vs. AISI 441 Stainless Steel

C66900 brass belongs to the copper alloys classification, while AISI 441 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C66900 brass and the bottom bar is AISI 441 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 120
200
Elongation at Break, % 1.1 to 26
23
Poisson's Ratio 0.32
0.28
Rockwell B Hardness 65 to 100
77
Shear Modulus, GPa 45
77
Shear Strength, MPa 290 to 440
300
Tensile Strength: Ultimate (UTS), MPa 460 to 770
470
Tensile Strength: Yield (Proof), MPa 330 to 760
270

Thermal Properties

Latent Heat of Fusion, J/g 190
280
Maximum Temperature: Mechanical, °C 150
910
Melting Completion (Liquidus), °C 860
1440
Melting Onset (Solidus), °C 850
1400
Specific Heat Capacity, J/kg-K 400
480
Thermal Expansion, µm/m-K 20
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 3.4
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 3.8
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 23
13
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 2.8
2.8
Embodied Energy, MJ/kg 46
41
Embodied Water, L/kg 310
130

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 4.6 to 200
92
Resilience: Unit (Modulus of Resilience), kJ/m3 460 to 2450
190
Stiffness to Weight: Axial, points 8.1
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 15 to 26
17
Strength to Weight: Bending, points 16 to 23
17
Thermal Shock Resistance, points 14 to 23
16

Alloy Composition

Carbon (C), % 0
0 to 0.030
Chromium (Cr), % 0
17.5 to 19.5
Copper (Cu), % 62.5 to 64.5
0
Iron (Fe), % 0 to 0.25
76 to 82.2
Lead (Pb), % 0 to 0.050
0
Manganese (Mn), % 11.5 to 12.5
0 to 1.0
Nickel (Ni), % 0
0 to 1.0
Niobium (Nb), % 0
0.3 to 0.9
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Titanium (Ti), % 0
0.1 to 0.5
Zinc (Zn), % 22.5 to 26
0
Residuals, % 0 to 0.2
0