C66900 Brass vs. EN 1.1221 Steel
C66900 brass belongs to the copper alloys classification, while EN 1.1221 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C66900 brass and the bottom bar is EN 1.1221 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 1.1 to 26 | |
| 10 to 21 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 45 | |
| 72 |
| Shear Strength, MPa | 290 to 440 | |
| 450 to 520 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 770 | |
| 730 to 870 |
| Tensile Strength: Yield (Proof), MPa | 330 to 760 | |
| 390 to 550 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 400 |
| Melting Completion (Liquidus), °C | 860 | |
| 1460 |
| Melting Onset (Solidus), °C | 850 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.4 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.8 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 2.1 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 1.5 |
| Embodied Energy, MJ/kg | 46 | |
| 19 |
| Embodied Water, L/kg | 310 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.6 to 200 | |
| 67 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 to 2450 | |
| 410 to 800 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 26 | |
| 26 to 31 |
| Strength to Weight: Bending, points | 16 to 23 | |
| 23 to 26 |
| Thermal Shock Resistance, points | 14 to 23 | |
| 23 to 28 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.57 to 0.65 |
| Chromium (Cr), % | 0 | |
| 0 to 0.4 |
| Copper (Cu), % | 62.5 to 64.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 97.1 to 98.8 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 11.5 to 12.5 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 | |
| 0 to 0.035 |
| Zinc (Zn), % | 22.5 to 26 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |