C66900 Brass vs. EN 1.4542 Stainless Steel
C66900 brass belongs to the copper alloys classification, while EN 1.4542 stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C66900 brass and the bottom bar is EN 1.4542 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 190 |
| Elongation at Break, % | 1.1 to 26 | |
| 5.7 to 20 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 45 | |
| 76 |
| Shear Strength, MPa | 290 to 440 | |
| 550 to 860 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 770 | |
| 880 to 1470 |
| Tensile Strength: Yield (Proof), MPa | 330 to 760 | |
| 580 to 1300 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 860 |
| Melting Completion (Liquidus), °C | 860 | |
| 1430 |
| Melting Onset (Solidus), °C | 850 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Expansion, µm/m-K | 20 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.4 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.8 | |
| 2.8 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 13 |
| Density, g/cm3 | 8.2 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 46 | |
| 39 |
| Embodied Water, L/kg | 310 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.6 to 200 | |
| 62 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 to 2450 | |
| 880 to 4360 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 15 to 26 | |
| 31 to 52 |
| Strength to Weight: Bending, points | 16 to 23 | |
| 26 to 37 |
| Thermal Shock Resistance, points | 14 to 23 | |
| 29 to 49 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.070 |
| Chromium (Cr), % | 0 | |
| 15 to 17 |
| Copper (Cu), % | 62.5 to 64.5 | |
| 3.0 to 5.0 |
| Iron (Fe), % | 0 to 0.25 | |
| 69.6 to 79 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 11.5 to 12.5 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.6 |
| Nickel (Ni), % | 0 | |
| 3.0 to 5.0 |
| Niobium (Nb), % | 0 | |
| 0 to 0.45 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Zinc (Zn), % | 22.5 to 26 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |