C66900 Brass vs. Grade CW6MC Nickel
C66900 brass belongs to the copper alloys classification, while grade CW6MC nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is C66900 brass and the bottom bar is grade CW6MC nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 200 |
| Elongation at Break, % | 1.1 to 26 | |
| 28 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 45 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 770 | |
| 540 |
| Tensile Strength: Yield (Proof), MPa | 330 to 760 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 980 |
| Melting Completion (Liquidus), °C | 860 | |
| 1480 |
| Melting Onset (Solidus), °C | 850 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 440 |
| Thermal Expansion, µm/m-K | 20 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.4 | |
| 1.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.8 | |
| 1.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 80 |
| Density, g/cm3 | 8.2 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 14 |
| Embodied Energy, MJ/kg | 46 | |
| 200 |
| Embodied Water, L/kg | 310 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 4.6 to 200 | |
| 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 460 to 2450 | |
| 240 |
| Stiffness to Weight: Axial, points | 8.1 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 23 |
| Strength to Weight: Axial, points | 15 to 26 | |
| 18 |
| Strength to Weight: Bending, points | 16 to 23 | |
| 17 |
| Thermal Shock Resistance, points | 14 to 23 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0 | |
| 20 to 23 |
| Copper (Cu), % | 62.5 to 64.5 | |
| 0 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 5.0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 11.5 to 12.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 8.0 to 10 |
| Nickel (Ni), % | 0 | |
| 55.4 to 68.9 |
| Niobium (Nb), % | 0 | |
| 3.2 to 4.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.015 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zinc (Zn), % | 22.5 to 26 | |
| 0 |
| Residuals, % | 0 to 0.2 | |
| 0 |