C66900 Brass vs. Solder Alloy 117
C66900 brass belongs to the copper alloys classification, while solder alloy 117 belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C66900 brass and the bottom bar is solder alloy 117.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 23 |
| Elongation at Break, % | 1.1 to 26 | |
| 20 |
| Poisson's Ratio | 0.32 | |
| 0.42 |
| Shear Modulus, GPa | 45 | |
| 8.1 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 770 | |
| 33 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 31 |
| Melting Completion (Liquidus), °C | 860 | |
| 280 |
| Melting Onset (Solidus), °C | 850 | |
| 180 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 150 |
| Thermal Expansion, µm/m-K | 20 | |
| 28 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.4 | |
| 8.7 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.8 | |
| 7.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 85 |
| Density, g/cm3 | 8.2 | |
| 11 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 6.1 |
| Embodied Energy, MJ/kg | 46 | |
| 100 |
| Embodied Water, L/kg | 310 | |
| 610 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.1 | |
| 1.2 |
| Stiffness to Weight: Bending, points | 20 | |
| 9.0 |
| Strength to Weight: Axial, points | 15 to 26 | |
| 0.88 |
| Strength to Weight: Bending, points | 16 to 23 | |
| 2.2 |
| Thermal Shock Resistance, points | 14 to 23 | |
| 3.7 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.5 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.25 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Copper (Cu), % | 62.5 to 64.5 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 to 0.050 | |
| 78.4 to 80.5 |
| Manganese (Mn), % | 11.5 to 12.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 | |
| 0 to 0.1 |
| Tin (Sn), % | 0 | |
| 19.5 to 20.5 |
| Zinc (Zn), % | 22.5 to 26 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.2 | |
| 0 |