C66900 Brass vs. C70250 Copper
Both C66900 brass and C70250 copper are copper alloys. They have 64% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C66900 brass and the bottom bar is C70250 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Poisson's Ratio | 0.32 | |
| 0.34 |
| Shear Modulus, GPa | 45 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 770 | |
| 520 to 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 220 |
| Maximum Temperature: Mechanical, °C | 150 | |
| 210 |
| Melting Completion (Liquidus), °C | 860 | |
| 1100 |
| Melting Onset (Solidus), °C | 850 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Expansion, µm/m-K | 20 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.4 | |
| 36 to 50 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.8 | |
| 37 to 51 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 31 |
| Density, g/cm3 | 8.2 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.9 |
| Embodied Energy, MJ/kg | 46 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 8.1 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 20 | |
| 18 |
| Strength to Weight: Axial, points | 15 to 26 | |
| 16 to 23 |
| Strength to Weight: Bending, points | 16 to 23 | |
| 16 to 21 |
| Thermal Shock Resistance, points | 14 to 23 | |
| 18 to 26 |
Alloy Composition
| Copper (Cu), % | 62.5 to 64.5 | |
| 92.7 to 97.5 |
| Iron (Fe), % | 0 to 0.25 | |
| 0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0 | |
| 0.050 to 0.3 |
| Manganese (Mn), % | 11.5 to 12.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 | |
| 2.2 to 4.2 |
| Silicon (Si), % | 0 | |
| 0.25 to 1.2 |
| Zinc (Zn), % | 22.5 to 26 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |