C67000 Bronze vs. EN 1.4313 Stainless Steel
C67000 bronze belongs to the copper alloys classification, while EN 1.4313 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C67000 bronze and the bottom bar is EN 1.4313 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 5.6 to 11 | |
| 12 to 17 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 76 |
| Shear Strength, MPa | 390 to 510 | |
| 460 to 600 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 880 | |
| 750 to 1000 |
| Tensile Strength: Yield (Proof), MPa | 350 to 540 | |
| 580 to 910 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 780 |
| Melting Completion (Liquidus), °C | 900 | |
| 1450 |
| Melting Onset (Solidus), °C | 850 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 480 |
| Thermal Conductivity, W/m-K | 99 | |
| 25 |
| Thermal Expansion, µm/m-K | 20 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 22 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 25 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 10 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 2.4 |
| Embodied Energy, MJ/kg | 49 | |
| 34 |
| Embodied Water, L/kg | 350 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 62 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 560 to 1290 | |
| 870 to 2100 |
| Stiffness to Weight: Axial, points | 7.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 31 | |
| 27 to 36 |
| Strength to Weight: Bending, points | 21 to 26 | |
| 23 to 28 |
| Thermal Diffusivity, mm2/s | 30 | |
| 6.7 |
| Thermal Shock Resistance, points | 21 to 29 | |
| 27 to 36 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 6.0 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 12 to 14 |
| Copper (Cu), % | 63 to 68 | |
| 0 |
| Iron (Fe), % | 2.0 to 4.0 | |
| 78.5 to 84.2 |
| Lead (Pb), % | 0 to 0.2 | |
| 0 |
| Manganese (Mn), % | 2.5 to 5.0 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 0.3 to 0.7 |
| Nickel (Ni), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.7 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Tin (Sn), % | 0 to 0.5 | |
| 0 |
| Zinc (Zn), % | 21.8 to 32.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |