C67400 Bronze vs. ASTM B540 Palladium
C67400 bronze belongs to the copper alloys classification, while ASTM B540 palladium belongs to the otherwise unclassified metals. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is C67400 bronze and the bottom bar is ASTM B540 palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 110 |
| Elongation at Break, % | 22 to 28 | |
| 1.1 to 14 |
| Poisson's Ratio | 0.31 | |
| 0.38 |
| Shear Modulus, GPa | 41 | |
| 39 |
| Shear Strength, MPa | 310 to 350 | |
| 500 to 700 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 610 | |
| 830 to 1240 |
| Tensile Strength: Yield (Proof), MPa | 250 to 370 | |
| 620 to 1000 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 140 |
| Melting Completion (Liquidus), °C | 890 | |
| 1220 |
| Melting Onset (Solidus), °C | 870 | |
| 1020 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 240 |
| Thermal Expansion, µm/m-K | 21 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 23 | |
| 4.9 to 5.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 26 | |
| 3.5 to 3.9 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.9 | |
| 13 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
| 13 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 660 | |
| 1790 to 4660 |
| Stiffness to Weight: Axial, points | 7.5 | |
| 4.7 |
| Stiffness to Weight: Bending, points | 20 | |
| 12 |
| Strength to Weight: Axial, points | 17 to 22 | |
| 18 to 27 |
| Strength to Weight: Bending, points | 17 to 20 | |
| 15 to 20 |
| Thermal Shock Resistance, points | 16 to 20 | |
| 41 to 61 |
Alloy Composition
| Aluminum (Al), % | 0.5 to 2.0 | |
| 0 |
| Copper (Cu), % | 57 to 60 | |
| 13.5 to 14.5 |
| Gold (Au), % | 0 | |
| 9.5 to 10.5 |
| Iron (Fe), % | 0 to 0.35 | |
| 0 |
| Lead (Pb), % | 0 to 0.5 | |
| 0 |
| Manganese (Mn), % | 2.0 to 3.5 | |
| 0 |
| Nickel (Ni), % | 0 to 0.25 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 34 to 36 |
| Platinum (Pt), % | 0 | |
| 9.5 to 10.5 |
| Silicon (Si), % | 0.5 to 1.5 | |
| 0 |
| Silver (Ag), % | 0 | |
| 29 to 31 |
| Tin (Sn), % | 0 to 0.3 | |
| 0 |
| Zinc (Zn), % | 31.1 to 40 | |
| 0.8 to 1.2 |
| Residuals, % | 0 | |
| 0 to 0.3 |