C67600 Bronze vs. EN 1.4105 Stainless Steel

C67600 bronze belongs to the copper alloys classification, while EN 1.4105 stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is C67600 bronze and the bottom bar is EN 1.4105 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
200
Elongation at Break, % 13 to 33
23
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 40
77
Shear Strength, MPa 270 to 350
340
Tensile Strength: Ultimate (UTS), MPa 430 to 570
530
Tensile Strength: Yield (Proof), MPa 170 to 380
290

Thermal Properties

Latent Heat of Fusion, J/g 170
290
Maximum Temperature: Mechanical, °C 120
870
Melting Completion (Liquidus), °C 890
1430
Melting Onset (Solidus), °C 870
1390
Specific Heat Capacity, J/kg-K 380
480
Thermal Conductivity, W/m-K 110
25
Thermal Expansion, µm/m-K 21
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 24
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 27
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 23
9.0
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 2.8
2.2
Embodied Energy, MJ/kg 47
31
Embodied Water, L/kg 330
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 63 to 130
100
Resilience: Unit (Modulus of Resilience), kJ/m3 140 to 680
210
Stiffness to Weight: Axial, points 7.2
14
Stiffness to Weight: Bending, points 20
25
Strength to Weight: Axial, points 15 to 20
19
Strength to Weight: Bending, points 16 to 19
19
Thermal Diffusivity, mm2/s 35
6.7
Thermal Shock Resistance, points 14 to 19
19

Alloy Composition

Carbon (C), % 0
0 to 0.080
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 57 to 60
0
Iron (Fe), % 0.4 to 1.3
77.9 to 83.7
Lead (Pb), % 0.5 to 1.0
0
Manganese (Mn), % 0.050 to 0.5
0 to 1.5
Molybdenum (Mo), % 0
0.2 to 0.6
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.5
Sulfur (S), % 0
0.15 to 0.35
Tin (Sn), % 0.5 to 1.5
0
Zinc (Zn), % 35.2 to 41.6
0
Residuals, % 0 to 0.5
0