C67600 Bronze vs. Grade 4 Titanium
C67600 bronze belongs to the copper alloys classification, while grade 4 titanium belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C67600 bronze and the bottom bar is grade 4 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Elongation at Break, % | 13 to 33 | |
| 17 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 41 |
| Shear Strength, MPa | 270 to 350 | |
| 390 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 570 | |
| 640 |
| Tensile Strength: Yield (Proof), MPa | 170 to 380 | |
| 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 420 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 320 |
| Melting Completion (Liquidus), °C | 890 | |
| 1660 |
| Melting Onset (Solidus), °C | 870 | |
| 1610 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 540 |
| Thermal Conductivity, W/m-K | 110 | |
| 19 |
| Thermal Expansion, µm/m-K | 21 | |
| 9.4 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 3.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 6.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 37 |
| Density, g/cm3 | 8.0 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 31 |
| Embodied Energy, MJ/kg | 47 | |
| 500 |
| Embodied Water, L/kg | 330 | |
| 110 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 to 130 | |
| 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 680 | |
| 1330 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 13 |
| Stiffness to Weight: Bending, points | 20 | |
| 35 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 40 |
| Strength to Weight: Bending, points | 16 to 19 | |
| 37 |
| Thermal Diffusivity, mm2/s | 35 | |
| 7.6 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 46 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Copper (Cu), % | 57 to 60 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 0.4 to 1.3 | |
| 0 to 0.5 |
| Lead (Pb), % | 0.5 to 1.0 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.4 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 98.6 to 100 |
| Zinc (Zn), % | 35.2 to 41.6 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.4 |