C67600 Bronze vs. C44300 Brass
Both C67600 bronze and C44300 brass are copper alloys. They have 87% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is C67600 bronze and the bottom bar is C44300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 110 |
| Poisson's Ratio | 0.31 | |
| 0.32 |
| Shear Modulus, GPa | 40 | |
| 41 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 570 | |
| 350 |
| Tensile Strength: Yield (Proof), MPa | 170 to 380 | |
| 120 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 180 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 140 |
| Melting Completion (Liquidus), °C | 890 | |
| 940 |
| Melting Onset (Solidus), °C | 870 | |
| 900 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 380 |
| Thermal Conductivity, W/m-K | 110 | |
| 110 |
| Thermal Expansion, µm/m-K | 21 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 26 |
| Density, g/cm3 | 8.0 | |
| 8.3 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 47 | |
| 46 |
| Embodied Water, L/kg | 330 | |
| 330 |
Common Calculations
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 680 | |
| 65 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 20 | |
| 19 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 12 |
| Strength to Weight: Bending, points | 16 to 19 | |
| 13 |
| Thermal Diffusivity, mm2/s | 35 | |
| 35 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 12 |
Alloy Composition
| Arsenic (As), % | 0 | |
| 0.020 to 0.060 |
| Copper (Cu), % | 57 to 60 | |
| 70 to 73 |
| Iron (Fe), % | 0.4 to 1.3 | |
| 0 to 0.060 |
| Lead (Pb), % | 0.5 to 1.0 | |
| 0 to 0.070 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0.9 to 1.2 |
| Zinc (Zn), % | 35.2 to 41.6 | |
| 25.2 to 29.1 |
| Residuals, % | 0 | |
| 0 to 0.4 |