C67600 Bronze vs. R30016 Cobalt
C67600 bronze belongs to the copper alloys classification, while R30016 cobalt belongs to the cobalt alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C67600 bronze and the bottom bar is R30016 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 220 |
| Elongation at Break, % | 13 to 33 | |
| 8.4 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 40 | |
| 85 |
| Tensile Strength: Ultimate (UTS), MPa | 430 to 570 | |
| 1010 |
| Tensile Strength: Yield (Proof), MPa | 170 to 380 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 170 | |
| 320 |
| Melting Completion (Liquidus), °C | 890 | |
| 1360 |
| Melting Onset (Solidus), °C | 870 | |
| 1270 |
| Specific Heat Capacity, J/kg-K | 380 | |
| 450 |
| Thermal Conductivity, W/m-K | 110 | |
| 15 |
| Thermal Expansion, µm/m-K | 21 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 24 | |
| 1.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 27 | |
| 2.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.0 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 7.7 |
| Embodied Energy, MJ/kg | 47 | |
| 110 |
| Embodied Water, L/kg | 330 | |
| 500 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 63 to 130 | |
| 72 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 to 680 | |
| 770 |
| Stiffness to Weight: Axial, points | 7.2 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 33 |
| Strength to Weight: Bending, points | 16 to 19 | |
| 26 |
| Thermal Diffusivity, mm2/s | 35 | |
| 3.9 |
| Thermal Shock Resistance, points | 14 to 19 | |
| 24 |
Alloy Composition
| Carbon (C), % | 0 | |
| 0.9 to 1.4 |
| Chromium (Cr), % | 0 | |
| 28 to 32 |
| Cobalt (Co), % | 0 | |
| 49.6 to 66.9 |
| Copper (Cu), % | 57 to 60 | |
| 0 |
| Iron (Fe), % | 0.4 to 1.3 | |
| 0 to 3.0 |
| Lead (Pb), % | 0.5 to 1.0 | |
| 0 |
| Manganese (Mn), % | 0.050 to 0.5 | |
| 0.5 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.5 |
| Nickel (Ni), % | 0 | |
| 0 to 3.0 |
| Silicon (Si), % | 0 | |
| 0.2 to 2.0 |
| Tin (Sn), % | 0.5 to 1.5 | |
| 0 |
| Tungsten (W), % | 0 | |
| 3.5 to 5.5 |
| Zinc (Zn), % | 35.2 to 41.6 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |