C68300 Brass vs. AISI 304N Stainless Steel
C68300 brass belongs to the copper alloys classification, while AISI 304N stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C68300 brass and the bottom bar is AISI 304N stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 15 | |
| 9.1 to 45 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 40 | |
| 77 |
| Shear Strength, MPa | 260 | |
| 420 to 700 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 620 to 1180 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 270 to 850 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 960 |
| Melting Completion (Liquidus), °C | 900 | |
| 1420 |
| Melting Onset (Solidus), °C | 890 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 120 | |
| 16 |
| Thermal Expansion, µm/m-K | 20 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 15 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.0 |
| Embodied Energy, MJ/kg | 46 | |
| 43 |
| Embodied Water, L/kg | 340 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 98 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 | |
| 180 to 1830 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 22 to 42 |
| Strength to Weight: Bending, points | 16 | |
| 21 to 32 |
| Thermal Diffusivity, mm2/s | 38 | |
| 4.2 |
| Thermal Shock Resistance, points | 14 | |
| 14 to 26 |
Alloy Composition
| Antimony (Sb), % | 0.3 to 1.0 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 18 to 20 |
| Copper (Cu), % | 59 to 63 | |
| 0 |
| Iron (Fe), % | 0 | |
| 66.4 to 73.9 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Nickel (Ni), % | 0 | |
| 8.0 to 10.5 |
| Nitrogen (N), % | 0 | |
| 0.1 to 0.16 |
| Phosphorus (P), % | 0 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.3 to 1.0 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0.050 to 0.2 | |
| 0 |
| Zinc (Zn), % | 34.2 to 40.4 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |