C68300 Brass vs. EN 1.4618 Stainless Steel
C68300 brass belongs to the copper alloys classification, while EN 1.4618 stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is C68300 brass and the bottom bar is EN 1.4618 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 15 | |
| 51 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 40 | |
| 77 |
| Shear Strength, MPa | 260 | |
| 480 to 500 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 680 to 700 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 250 to 260 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 900 |
| Melting Completion (Liquidus), °C | 900 | |
| 1400 |
| Melting Onset (Solidus), °C | 890 | |
| 1360 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 120 | |
| 15 |
| Thermal Expansion, µm/m-K | 20 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 13 |
| Density, g/cm3 | 8.0 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.7 |
| Embodied Energy, MJ/kg | 46 | |
| 39 |
| Embodied Water, L/kg | 340 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 270 to 280 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 | |
| 160 to 170 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 24 to 25 |
| Strength to Weight: Bending, points | 16 | |
| 22 to 23 |
| Thermal Diffusivity, mm2/s | 38 | |
| 4.0 |
| Thermal Shock Resistance, points | 14 | |
| 15 to 16 |
Alloy Composition
| Antimony (Sb), % | 0.3 to 1.0 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 16.5 to 18.5 |
| Copper (Cu), % | 59 to 63 | |
| 1.0 to 2.5 |
| Iron (Fe), % | 0 | |
| 62.7 to 72.5 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 5.5 to 9.5 |
| Nickel (Ni), % | 0 | |
| 4.5 to 5.5 |
| Nitrogen (N), % | 0 | |
| 0 to 0.15 |
| Phosphorus (P), % | 0 | |
| 0 to 0.070 |
| Silicon (Si), % | 0.3 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 0.050 to 0.2 | |
| 0 |
| Zinc (Zn), % | 34.2 to 40.4 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |