C68300 Brass vs. EN 1.7715 Steel

C68300 brass belongs to the copper alloys classification, while EN 1.7715 steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is C68300 brass and the bottom bar is EN 1.7715 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 100
190
Elongation at Break, % 15
21
Poisson's Ratio 0.31
0.29
Shear Modulus, GPa 40
73
Shear Strength, MPa 260
340
Tensile Strength: Ultimate (UTS), MPa 430
540
Tensile Strength: Yield (Proof), MPa 260
340

Thermal Properties

Latent Heat of Fusion, J/g 180
250
Maximum Temperature: Mechanical, °C 120
420
Melting Completion (Liquidus), °C 900
1470
Melting Onset (Solidus), °C 890
1430
Specific Heat Capacity, J/kg-K 390
470
Thermal Conductivity, W/m-K 120
40
Thermal Expansion, µm/m-K 20
13

Otherwise Unclassified Properties

Base Metal Price, % relative 23
2.9
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 2.8
2.2
Embodied Energy, MJ/kg 46
30
Embodied Water, L/kg 340
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 56
99
Resilience: Unit (Modulus of Resilience), kJ/m3 330
320
Stiffness to Weight: Axial, points 7.3
13
Stiffness to Weight: Bending, points 20
24
Strength to Weight: Axial, points 15
19
Strength to Weight: Bending, points 16
19
Thermal Diffusivity, mm2/s 38
11
Thermal Shock Resistance, points 14
16

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Antimony (Sb), % 0.3 to 1.0
0
Cadmium (Cd), % 0 to 0.010
0
Carbon (C), % 0
0.1 to 0.15
Chromium (Cr), % 0
0.3 to 0.6
Copper (Cu), % 59 to 63
0 to 0.3
Iron (Fe), % 0
96.5 to 98.3
Lead (Pb), % 0 to 0.090
0
Manganese (Mn), % 0
0.4 to 0.7
Molybdenum (Mo), % 0
0.5 to 0.7
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0.3 to 1.0
0.15 to 0.35
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 0.050 to 0.2
0
Vanadium (V), % 0
0.22 to 0.28
Zinc (Zn), % 34.2 to 40.4
0
Residuals, % 0 to 0.5
0