C68300 Brass vs. S45000 Stainless Steel
C68300 brass belongs to the copper alloys classification, while S45000 stainless steel belongs to the iron alloys. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is C68300 brass and the bottom bar is S45000 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 100 | |
| 200 |
| Elongation at Break, % | 15 | |
| 6.8 to 14 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 40 | |
| 76 |
| Shear Strength, MPa | 260 | |
| 590 to 830 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 980 to 1410 |
| Tensile Strength: Yield (Proof), MPa | 260 | |
| 580 to 1310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 180 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 120 | |
| 840 |
| Melting Completion (Liquidus), °C | 900 | |
| 1440 |
| Melting Onset (Solidus), °C | 890 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 480 |
| Thermal Conductivity, W/m-K | 120 | |
| 17 |
| Thermal Expansion, µm/m-K | 20 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 23 | |
| 13 |
| Density, g/cm3 | 8.0 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 46 | |
| 39 |
| Embodied Water, L/kg | 340 | |
| 130 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 56 | |
| 94 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 330 | |
| 850 to 4400 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 20 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 35 to 50 |
| Strength to Weight: Bending, points | 16 | |
| 28 to 36 |
| Thermal Diffusivity, mm2/s | 38 | |
| 4.5 |
| Thermal Shock Resistance, points | 14 | |
| 33 to 47 |
Alloy Composition
| Antimony (Sb), % | 0.3 to 1.0 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.010 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 14 to 16 |
| Copper (Cu), % | 59 to 63 | |
| 1.3 to 1.8 |
| Iron (Fe), % | 0 | |
| 72.1 to 79.3 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0.5 to 1.0 |
| Nickel (Ni), % | 0 | |
| 5.0 to 7.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.3 to 1.0 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 0.050 to 0.2 | |
| 0 |
| Zinc (Zn), % | 34.2 to 40.4 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |