C68700 Brass vs. R05240 Alloy

C68700 brass belongs to the copper alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is C68700 brass and the bottom bar is R05240 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 110
150
Poisson's Ratio 0.32
0.36
Shear Modulus, GPa 41
57
Tensile Strength: Ultimate (UTS), MPa 390
270
Tensile Strength: Yield (Proof), MPa 140
170

Thermal Properties

Latent Heat of Fusion, J/g 190
210
Specific Heat Capacity, J/kg-K 400
190
Thermal Expansion, µm/m-K 19
6.8

Otherwise Unclassified Properties

Density, g/cm3 8.3
14
Embodied Water, L/kg 340
460

Common Calculations

Resilience: Unit (Modulus of Resilience), kJ/m3 90
90
Stiffness to Weight: Axial, points 7.3
6.3
Stiffness to Weight: Bending, points 19
13
Strength to Weight: Axial, points 13
5.4
Strength to Weight: Bending, points 14
6.8
Thermal Shock Resistance, points 13
18

Alloy Composition

Aluminum (Al), % 1.8 to 2.5
0
Arsenic (As), % 0.020 to 0.1
0
Carbon (C), % 0
0 to 0.010
Copper (Cu), % 76 to 79
0
Hydrogen (H), % 0
0 to 0.0015
Iron (Fe), % 0 to 0.060
0 to 0.010
Lead (Pb), % 0 to 0.070
0
Molybdenum (Mo), % 0
0 to 0.020
Nickel (Ni), % 0
0 to 0.010
Niobium (Nb), % 0
35 to 42
Nitrogen (N), % 0
0 to 0.010
Oxygen (O), % 0
0 to 0.020
Silicon (Si), % 0
0 to 0.0050
Tantalum (Ta), % 0
57.9 to 65
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
0 to 0.050
Zinc (Zn), % 17.8 to 22.2
0
Residuals, % 0 to 0.5
0