C68800 Brass vs. C67500 Bronze
Both C68800 brass and C67500 bronze are copper alloys. They have 82% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is C68800 brass and the bottom bar is C67500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 100 |
| Elongation at Break, % | 2.0 to 36 | |
| 14 to 33 |
| Poisson's Ratio | 0.32 | |
| 0.3 |
| Shear Modulus, GPa | 41 | |
| 40 |
| Shear Strength, MPa | 380 to 510 | |
| 270 to 350 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 890 | |
| 430 to 580 |
| Tensile Strength: Yield (Proof), MPa | 390 to 790 | |
| 170 to 370 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 120 |
| Melting Completion (Liquidus), °C | 960 | |
| 890 |
| Melting Onset (Solidus), °C | 950 | |
| 870 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 390 |
| Thermal Conductivity, W/m-K | 40 | |
| 110 |
| Thermal Expansion, µm/m-K | 19 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 20 | |
| 27 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 23 |
| Density, g/cm3 | 8.2 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 2.8 |
| Embodied Energy, MJ/kg | 48 | |
| 47 |
| Embodied Water, L/kg | 350 | |
| 330 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 180 | |
| 61 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 710 to 2860 | |
| 130 to 650 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 19 | |
| 20 |
| Strength to Weight: Axial, points | 19 to 30 | |
| 15 to 20 |
| Strength to Weight: Bending, points | 19 to 25 | |
| 16 to 19 |
| Thermal Diffusivity, mm2/s | 12 | |
| 34 |
| Thermal Shock Resistance, points | 19 to 30 | |
| 14 to 19 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 3.8 | |
| 0 to 0.25 |
| Cobalt (Co), % | 0.25 to 0.55 | |
| 0 |
| Copper (Cu), % | 70.8 to 75.5 | |
| 57 to 60 |
| Iron (Fe), % | 0 to 0.2 | |
| 0.8 to 2.0 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.2 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.5 |
| Tin (Sn), % | 0 | |
| 0.5 to 1.5 |
| Zinc (Zn), % | 21.3 to 24.1 | |
| 35.1 to 41.7 |
| Residuals, % | 0 | |
| 0 to 0.5 |