C68800 Brass vs. S45500 Stainless Steel
C68800 brass belongs to the copper alloys classification, while S45500 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is C68800 brass and the bottom bar is S45500 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 190 |
| Elongation at Break, % | 2.0 to 36 | |
| 3.4 to 11 |
| Poisson's Ratio | 0.32 | |
| 0.28 |
| Shear Modulus, GPa | 41 | |
| 75 |
| Shear Strength, MPa | 380 to 510 | |
| 790 to 1090 |
| Tensile Strength: Ultimate (UTS), MPa | 570 to 890 | |
| 1370 to 1850 |
| Tensile Strength: Yield (Proof), MPa | 390 to 790 | |
| 1240 to 1700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 190 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 160 | |
| 760 |
| Melting Completion (Liquidus), °C | 960 | |
| 1440 |
| Melting Onset (Solidus), °C | 950 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 470 |
| Thermal Expansion, µm/m-K | 19 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 17 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 2.8 | |
| 3.8 |
| Embodied Energy, MJ/kg | 48 | |
| 57 |
| Embodied Water, L/kg | 350 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 16 to 180 | |
| 45 to 190 |
| Stiffness to Weight: Axial, points | 7.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 30 | |
| 48 to 65 |
| Strength to Weight: Bending, points | 19 to 25 | |
| 35 to 42 |
| Thermal Shock Resistance, points | 19 to 30 | |
| 48 to 64 |
Alloy Composition
| Aluminum (Al), % | 3.0 to 3.8 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.050 |
| Chromium (Cr), % | 0 | |
| 11 to 12.5 |
| Cobalt (Co), % | 0.25 to 0.55 | |
| 0 |
| Copper (Cu), % | 70.8 to 75.5 | |
| 1.5 to 2.5 |
| Iron (Fe), % | 0 to 0.2 | |
| 71.5 to 79.2 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 7.5 to 9.5 |
| Niobium (Nb), % | 0 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0 | |
| 0.8 to 1.4 |
| Zinc (Zn), % | 21.3 to 24.1 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |