C69300 Brass vs. Commercially Pure Palladium
C69300 brass belongs to the copper alloys classification, while commercially pure palladium belongs to the otherwise unclassified metals. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C69300 brass and the bottom bar is commercially pure palladium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 120 |
| Elongation at Break, % | 8.5 to 15 | |
| 1.1 to 11 |
| Poisson's Ratio | 0.32 | |
| 0.39 |
| Shear Modulus, GPa | 41 | |
| 43 |
| Shear Strength, MPa | 330 to 370 | |
| 120 to 200 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 630 | |
| 200 to 380 |
Thermal Properties
| Latent Heat of Fusion, J/g | 240 | |
| 160 |
| Melting Completion (Liquidus), °C | 880 | |
| 1550 |
| Melting Onset (Solidus), °C | 860 | |
| 1550 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 240 |
| Thermal Expansion, µm/m-K | 19 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 16 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 12 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 5.6 |
| Stiffness to Weight: Bending, points | 19 | |
| 14 |
| Strength to Weight: Axial, points | 19 to 21 | |
| 4.5 to 8.8 |
| Strength to Weight: Bending, points | 18 to 20 | |
| 6.2 to 9.7 |
| Thermal Shock Resistance, points | 19 to 22 | |
| 9.8 to 19 |
Alloy Composition
| Copper (Cu), % | 73 to 77 | |
| 0 |
| Iron (Fe), % | 0 to 0.1 | |
| 0 |
| Lead (Pb), % | 0 to 0.090 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.1 | |
| 0 |
| Palladium (Pd), % | 0 | |
| 99.8 to 100 |
| Phosphorus (P), % | 0.040 to 0.15 | |
| 0 |
| Silicon (Si), % | 2.7 to 3.4 | |
| 0 |
| Tin (Sn), % | 0 to 0.2 | |
| 0 |
| Zinc (Zn), % | 18.4 to 24.3 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.2 |