C69430 Brass vs. AISI 440A Stainless Steel
C69430 brass belongs to the copper alloys classification, while AISI 440A stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C69430 brass and the bottom bar is AISI 440A stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 200 |
| Elongation at Break, % | 17 | |
| 5.0 to 20 |
| Poisson's Ratio | 0.33 | |
| 0.28 |
| Shear Modulus, GPa | 42 | |
| 77 |
| Shear Strength, MPa | 350 | |
| 450 to 1040 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 730 to 1790 |
| Tensile Strength: Yield (Proof), MPa | 280 | |
| 420 to 1650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 760 |
| Melting Completion (Liquidus), °C | 920 | |
| 1480 |
| Melting Onset (Solidus), °C | 820 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 480 |
| Thermal Conductivity, W/m-K | 26 | |
| 23 |
| Thermal Expansion, µm/m-K | 18 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.2 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 6.7 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 9.0 |
| Density, g/cm3 | 8.3 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 2.2 |
| Embodied Energy, MJ/kg | 44 | |
| 31 |
| Embodied Water, L/kg | 300 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 80 | |
| 87 to 120 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 25 |
| Strength to Weight: Axial, points | 19 | |
| 26 to 65 |
| Strength to Weight: Bending, points | 18 | |
| 23 to 43 |
| Thermal Diffusivity, mm2/s | 7.7 | |
| 6.2 |
| Thermal Shock Resistance, points | 20 | |
| 26 to 65 |
Alloy Composition
| Arsenic (As), % | 0.030 to 0.060 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.6 to 0.75 |
| Chromium (Cr), % | 0 | |
| 16 to 18 |
| Copper (Cu), % | 80 to 83 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 78.4 to 83.4 |
| Lead (Pb), % | 0 to 0.3 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.75 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 3.5 to 4.5 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.015 |
| Zinc (Zn), % | 11.4 to 16.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |