C69430 Brass vs. Grade CX2M Nickel
C69430 brass belongs to the copper alloys classification, while grade CX2M nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C69430 brass and the bottom bar is grade CX2M nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 110 | |
| 220 |
| Elongation at Break, % | 17 | |
| 45 |
| Poisson's Ratio | 0.33 | |
| 0.29 |
| Shear Modulus, GPa | 42 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 550 |
| Tensile Strength: Yield (Proof), MPa | 280 | |
| 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 330 |
| Maximum Temperature: Mechanical, °C | 170 | |
| 990 |
| Melting Completion (Liquidus), °C | 920 | |
| 1500 |
| Melting Onset (Solidus), °C | 820 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 410 | |
| 430 |
| Thermal Conductivity, W/m-K | 26 | |
| 10 |
| Thermal Expansion, µm/m-K | 18 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 27 | |
| 65 |
| Density, g/cm3 | 8.3 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 12 |
| Embodied Energy, MJ/kg | 44 | |
| 160 |
| Embodied Water, L/kg | 300 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 80 | |
| 210 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 340 | |
| 220 |
| Stiffness to Weight: Axial, points | 7.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 19 | |
| 23 |
| Strength to Weight: Axial, points | 19 | |
| 18 |
| Strength to Weight: Bending, points | 18 | |
| 17 |
| Thermal Diffusivity, mm2/s | 7.7 | |
| 2.7 |
| Thermal Shock Resistance, points | 20 | |
| 15 |
Alloy Composition
| Arsenic (As), % | 0.030 to 0.060 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.020 |
| Chromium (Cr), % | 0 | |
| 22 to 24 |
| Copper (Cu), % | 80 to 83 | |
| 0 |
| Iron (Fe), % | 0 to 0.2 | |
| 0 to 1.5 |
| Lead (Pb), % | 0 to 0.3 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 15 to 16.5 |
| Nickel (Ni), % | 0 | |
| 56.4 to 63 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 3.5 to 4.5 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Zinc (Zn), % | 11.4 to 16.5 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |