C70250 Copper vs. C14510 Copper
Both C70250 copper and C14510 copper are copper alloys. They have a very high 95% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is C70250 copper and the bottom bar is C14510 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 120 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 740 | |
| 300 to 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 200 |
| Melting Completion (Liquidus), °C | 1100 | |
| 1080 |
| Melting Onset (Solidus), °C | 1080 | |
| 1050 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 390 |
| Thermal Conductivity, W/m-K | 170 | |
| 360 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 33 |
| Density, g/cm3 | 8.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 2.6 |
| Embodied Energy, MJ/kg | 45 | |
| 42 |
| Embodied Water, L/kg | 310 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 18 | |
| 18 |
| Strength to Weight: Axial, points | 16 to 23 | |
| 9.2 to 10 |
| Strength to Weight: Bending, points | 16 to 21 | |
| 11 to 12 |
| Thermal Diffusivity, mm2/s | 49 | |
| 100 |
| Thermal Shock Resistance, points | 18 to 26 | |
| 11 to 12 |
Alloy Composition
| Copper (Cu), % | 92.7 to 97.5 | |
| 99.15 to 99.69 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0.050 to 0.3 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 2.2 to 4.2 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0.010 to 0.030 |
| Silicon (Si), % | 0.25 to 1.2 | |
| 0 |
| Tellurium (Te), % | 0 | |
| 0.3 to 0.7 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 |
| Residuals, % | 0 to 0.5 | |
| 0 |