C70250 Copper vs. C63800 Bronze
Both C70250 copper and C63800 bronze are copper alloys. They have a very high 96% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is C70250 copper and the bottom bar is C63800 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 110 |
| Poisson's Ratio | 0.34 | |
| 0.34 |
| Shear Modulus, GPa | 44 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 740 | |
| 460 to 1010 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 240 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 200 |
| Melting Completion (Liquidus), °C | 1100 | |
| 1030 |
| Melting Onset (Solidus), °C | 1080 | |
| 1000 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 410 |
| Thermal Conductivity, W/m-K | 170 | |
| 40 |
| Thermal Expansion, µm/m-K | 17 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 to 50 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 to 51 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 30 |
| Density, g/cm3 | 8.9 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 2.8 |
| Embodied Energy, MJ/kg | 45 | |
| 45 |
| Embodied Water, L/kg | 310 | |
| 330 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 18 | |
| 19 |
| Strength to Weight: Axial, points | 16 to 23 | |
| 15 to 33 |
| Strength to Weight: Bending, points | 16 to 21 | |
| 15 to 26 |
| Thermal Diffusivity, mm2/s | 49 | |
| 11 |
| Thermal Shock Resistance, points | 18 to 26 | |
| 17 to 36 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 2.5 to 3.1 |
| Cobalt (Co), % | 0 | |
| 0.25 to 0.55 |
| Copper (Cu), % | 92.7 to 97.5 | |
| 92.4 to 95.8 |
| Iron (Fe), % | 0 | |
| 0 to 0.2 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.050 |
| Magnesium (Mg), % | 0.050 to 0.3 | |
| 0 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 0.1 |
| Nickel (Ni), % | 2.2 to 4.2 | |
| 0 to 0.2 |
| Silicon (Si), % | 0.25 to 1.2 | |
| 1.5 to 2.1 |
| Zinc (Zn), % | 0 to 1.0 | |
| 0 to 0.8 |
| Residuals, % | 0 | |
| 0 to 0.5 |