C70250 Copper vs. ZA-12
C70250 copper belongs to the copper alloys classification, while ZA-12 belongs to the zinc alloys. There are 24 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is C70250 copper and the bottom bar is ZA-12.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 83 |
| Poisson's Ratio | 0.34 | |
| 0.26 |
| Shear Modulus, GPa | 44 | |
| 33 |
| Tensile Strength: Ultimate (UTS), MPa | 520 to 740 | |
| 260 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 220 | |
| 120 |
| Maximum Temperature: Mechanical, °C | 210 | |
| 100 |
| Melting Completion (Liquidus), °C | 1100 | |
| 430 |
| Melting Onset (Solidus), °C | 1080 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 390 | |
| 450 |
| Thermal Conductivity, W/m-K | 170 | |
| 120 |
| Thermal Expansion, µm/m-K | 17 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 36 to 50 | |
| 28 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 37 to 51 | |
| 42 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 11 |
| Density, g/cm3 | 8.9 | |
| 6.0 |
| Embodied Carbon, kg CO2/kg material | 2.9 | |
| 3.4 |
| Embodied Energy, MJ/kg | 45 | |
| 64 |
| Embodied Water, L/kg | 310 | |
| 440 |
Common Calculations
| Stiffness to Weight: Axial, points | 7.4 | |
| 7.6 |
| Stiffness to Weight: Bending, points | 18 | |
| 24 |
| Strength to Weight: Axial, points | 16 to 23 | |
| 12 to 19 |
| Strength to Weight: Bending, points | 16 to 21 | |
| 15 to 20 |
| Thermal Diffusivity, mm2/s | 49 | |
| 43 |
| Thermal Shock Resistance, points | 18 to 26 | |
| 9.4 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 10.5 to 11.5 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Copper (Cu), % | 92.7 to 97.5 | |
| 0.5 to 1.2 |
| Iron (Fe), % | 0 | |
| 0 to 0.075 |
| Lead (Pb), % | 0 to 0.050 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0.050 to 0.3 | |
| 0.015 to 0.030 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 2.2 to 4.2 | |
| 0 to 0.020 |
| Silicon (Si), % | 0.25 to 1.2 | |
| 0 to 0.060 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 to 1.0 | |
| 87.1 to 89 |
| Residuals, % | 0 to 0.5 | |
| 0 |